A first dielectric layer 3, a multilayer magnetic film 10 in which a first magnetic layer 4 having perpendicular magnetic anisotropy at room temperature, a second magnetic layer 5 having inplane magnetic anisotropy at room temperature, and a third magnetic layer 6 having perpendicular magnetic anisotropy at room temperature are sequentially laminated, a second dielectric layer 7, a reflective layer 8, and a protective layer 9 are sequentially laminated onto one principal plane of a disk substrate 2 on which a land and a groove exist, thereby forming a magnetooptic disk 1. Saturation magnetization of the second magnetic layer 5 is set to a range from 8.80.times.10.sup.-2 to 1.76.times.10.sup.-1 Wb/m.sup.2. A gas pressure upon film creation of the second magnetic layer is set to a range from 0.6 to 3.0 Pa. A content ratio of Co in the third magnetic layer 6 is set to a range from 15 to 17 atom %.