The invention relates to a low-density polyethylene resin for laminates, a composition thereof, and a laminate and production method therefor. The low-density polyethylene resin is one obtainable by a high pressure radical polymerization method and has a density of 0.910 to 0.935 g/cm.sup.3, a melt flow rate of 0.1 to 300 g/10 min., and a terminal vinyl group number of 0.4 or more per 1,000 carbon atoms. According to the invention, a laminate having high interlayer adhesion strength can be obtained also by low-temperature, high-speed molding so that the occurrence of smoking and odor can be prevented. Also, the resin is excellent in productivity and economics. Further, the resin is excellent in productivity and economics because it can be readily made thinner. The laminate is suitable for application to, for example, food wrapping materials, containers, etc.

Η εφεύρεση αφορά μια low-density ρητίνη πολυαιθυλενίου για τα φύλλα πλαστικού, μια σύνθεση επ' αυτού, και μια μέθοδο φύλλων πλαστικού και παραγωγής γί αυτό. Η low-density ρητίνη πολυαιθυλενίου είναι ένα αποκτήσιμο με μια υψηλή μέθοδο πολυμερισμού πίεσης ριζική και έχει μια πυκνότητα 0,910 έως 0,935 γ/cm.sup.3, ενός ποσοστού ροής λειωμένων μετάλλων 0,1 έως 300 g/10 λεπτά, και ενός τελικού βινυλίου αριθμού ομάδας 0,4 ή περισσότεροι ανά 1.000 άτομα άνθρακα. Σύμφωνα με την εφεύρεση, ένα φύλλο πλαστικού που έχει την υψηλή δύναμη προσκόλλησης ενδιάμεσων στρωμάτων μπορεί να ληφθεί επίσης από χαμηλής θερμοκρασίας, μεγάλη ταχύτητα που φορμάρει έτσι ώστε περιστατικό του καπνίσματος και της μυρωδιάς μπορεί να αποτραπεί. Επίσης, η ρητίνη είναι άριστη στην παραγωγικότητα και τα οικονομικά. Περαιτέρω, η ρητίνη είναι άριστη στην παραγωγικότητα και τα οικονομικά επειδή μπορεί να γίνει εύκολα λεπτύτερη. Το φύλλο πλαστικού είναι κατάλληλο για την εφαρμογή, παραδείγματος χάριν, στα τυλίγοντας υλικά τροφίμων, τα εμπορευματοκιβώτια, κ.λπ....