A process for improving 6XXX alloys, such as 6013, preferably includes heating, hot rolling, inter-rolling thermal treatment at a very high temperature such as 1020.degree. F. or more, again hot rolling (with or without subsequent continuous hot rolling or cold rolling or both), solution heat treating and artificial aging. The initial heating, inter-rolling, thermal treatment and solution treatment, especially the latter two, are carried out at very high temperatures such as 1030.degree. F. Each aforesaid hot rolling stage produces substantial metal thickness reduction. The improved sheet or plate product has a substantially reduced occurrence of reduced density features revealed in scanning electron microscope examination at 500.times. and exhibits improved (reduced) fatigue crack growth rate providing an advantage in aerospace applications such as fuselage skin, especially fuselage belly skin.

Ein Prozeß für das Verbessern der Legierungen 6XXX, wie 6013, schließt vorzugsweise Heizung, heißes Rollen, Zwischen-Rollen thermische Behandlung an einem sehr Hochtemperatur wie 1020.degree ein. F. oder mehr, wieder heißes Rollen (mit oder ohne folgendes ununterbrochenes heißes Rollen oder Kälterollen oder -beide), Lösung Hitzebehandeln und künstliches Altern. Die Ausgangsheizung, das Zwischen-Rollen, die thermische Behandlung und die Lösung Behandlung, besonders die letzten zwei, werden bei den sehr hohen Temperaturen wie 1030.degree durchgeführt. F. Jedes vorher erwähnte Stadium des heißen Rollens produziert erhebliche Metallstärke Verkleinerung. Das verbesserte Blatt- oder Plattenprodukt hat ein im wesentlichen verringertes Auftreten der verringerten Dichteeigenschaften, die in der Rasterelektronenmikroskopprüfung mit 500.times. und Ausstellungen verbesserter aufgedeckt werden (verringerter) Ermüdungbruchfortschrittrate, die einen Vorteil in den Luftfahrtanwendungen wie Rumpfhaut, besonders Rumpfbauchhaut bereitstellen.