Provided is a novel olefin copolymer comprising [A] a cyclic olefin, [B] an
aromatic vinyl compound and [C] an aliphatic .alpha.-olefin having from 2
to 20 carbon atoms. (1) the component [A] therein accounts for from 0.1 to
30 mol %, the component [B] for from 0.1 to 49.9 mol %, and the total of
the components [A] and [B] for from 0.2 to 50 mol %; and (2) the copolymer
has a glass transition temperature Tg of lower than 60.degree. C. Having a
suitable modulus of elasticity, the copolymer can be a substitute for soft
polyvinyl chloride as a soft resin, and it has good elastic recovery and
transparency.
Si est un copolymère d'oléfine de roman comportant [ A ] une oléfine cyclique, [ B ] un vinyle aromatique composé et [ C ] une alpha.-oléfine aliphatique ayant de 2 à 20 atomes de carbone. (1) le composant [ A ] représente là-dedans 0.1 30 moles de %, le composant [ B ] pour 0.1 49.9 moles de %, et le total des composants [ A ] et [ B ] pour 0.2 50 moles de % ; et (2) le copolymère a une température de transition de verre Tg de inférieur à 60.degree. C. Ayant un module d'élasticité approprié, le copolymère peut être un produit de remplacement pour le chlorure polyvinylique mou comme résine molle, et il a le bon rétablissement élastique et le transparent.