Aluminum alloy die castings combine good as-cast strength with good as-cast
ductility, without any heat treatment. The alloy comprises 2.75 5.25 wt. %
magnesium, 1.85-3.15 wt. % zinc, 0.65-1.2 wt. % manganese, 0.10-0.18 wt. %
iron, less than 0.10 wt. % copper, less than 0.10 wt. % silicon, less than
0.20 wt. % titanium and the balance aluminum and incidental impurities and
furthermore the percent by weight magnesium is greater than or equal to
the percent by weight zinc. A particularly high strength version of the
alloy comprises 4.75%-5.25 wt. % magnesium and 2.85-3.15 wt. % zinc. A
particularly high ductility version of the alloy comprises 2.75-3.25 wt. %
magnesium, 1.85 2.5 wt. % zinc.
De afgietsels van de de legeringsmatrijs van het aluminium combineren goede gegoten sterkte met goede gegoten rekbaarheid, zonder enige thermische behandeling. De legering bestaat uit 2,75 5,25 % gew.- magnesium, 1.85-3.15 % gew.- zink, 0.65-1.2 % gew.- mangaan, 0.10-0.18 % gew.- ijzer, minder dan 0,10 % gew.- koper, minder dan 0,10 % gew.silicium, minder dan 0,20 % gew.titanium en de saldoaluminium en bijkomende onzuiverheden en verder is het percenten in gewicht magnesium groter dan of gelijk aan het percenten in gewicht zink. Een bijzonder hoge sterkteversie van de legering bestaat uit 4.75%-5.25 % gew. magnesium en 2.85-3.15 % gew.- zink. Een bijzonder hoge rekbaarheidsversie van de legering bestaat uit 2.75-3.25 % gew.- magnesium, 1,85 2,5 % gew.- zink.