This invention relates generally to crystalline polypropylene polymers and
methods for their production. Specifically, this invention relates to
crystalline polypropylene polymer compositions comprising both propylene
homopolymers and propylene copolymers. The compositions are prepared using
metallocene catalyst systems comprising at least two metallocenes in a
polymerization process that involves the sequential or parallel
polymerization of propylene homopolymers and copolymers using propylene
with a small amount of comonomer, preferably ethylene. The resulting
polymers are excellent for use in the production of biaxially oriented
films. Films prepared with these propylene polymers have a significantly
broader processability range and can be evenly stretched at lower
temperature compared to films prepared from traditional polypropylene
polymers.
Esta invención se relaciona generalmente con los polímeros cristalinos y los métodos del polypropylene para su producción. Específicamente, esta invención se relaciona con las composiciones cristalinas del polímero del polypropylene que abarcan los homopolímeros del propylene y los copolímeros del propylene. Las composiciones están preparadas usando los sistemas del catalizador del metallocene que abarcan por lo menos dos metallocenes en un proceso de la polimerización que implique la polimerización secuencial o paralela de los homopolímeros y de los copolímeros del propylene usando el propylene con una cantidad pequeña de comonomer, preferiblemente etileno. Los polímeros que resultan son excelentes para el uso en la producción de películas biaxial orientadas. Las películas se prepararon con estos polímeros del propylene tienen una gama perceptiblemente más amplia del processability y se pueden estirar uniformemente en una temperatura más baja comparada a las películas preparadas de los polímeros tradicionales del polypropylene.