Compositions, apparatus and methods of the present invention concern the
manufacturing parts that remain strong and dimensionally stable after
exposure to e-coat painting conditions. Such manufacturing includes
providing a molding compound having about 55-65% by weight polyethylene
terephthalate content, about 35-45% by weight filler content, and
optionally about 1% by weight blowing agent content. When an injection
molding machine is provided, the molding compound can be fed into the
injection molding machine to form a raw part. The raw part can then be
removed from the injection mold and quenched in a quenching bath to
produce a hardened part. The hardened part can then be secured to a
partially assembled vehicle. The hardened part, along with the rest of the
partially assembled vehicle can then be electro-coated, painted, and baked
to produce a final vehicle or sub-assembly thereof.
Aufbau, Apparate und Methoden der anwesenden Erfindung betreffen die Herstellung Teile, die stark und nach Aussetzung zu den Emantel Anstrichzuständen dimensional beständig bleiben. Solche Herstellung schließt das Zur Verfügung stellen eines Formteilmittels ein, das ungefähr 55-65% nach Gewicht Polyäthylenterephthalatinhalt, ungefähr 35-45% nach Gewicht Füllinhalt und beliebig ungefähr 1% nach Gewicht Treibmittelinhalt hat. Wenn eine Spritzenmaschine zur Verfügung gestellt wird, kann das Formteilmittel in die Spritzenmaschine eingezogen werden, um rohes Teil darzustellen. Das rohe Teil kann von der Einspritzungform dann entfernt werden und in einem löschenden Bad gelöscht werden, um ein verhärtetes Teil zu produzieren. Das verhärtete Teil kann an einen teilweise zusammengebauten Träger dann befestigt werden. Das verhärtete Teil, zusammen mit dem Rest des teilweise zusammengebauten Trägers kann electro-überzogen, gemalt, und gebacken dann sein, um einen abschließenden Träger oder eine Unterbaugruppe davon zu produzieren.