A method for coating particles and the coated particles obtained thereby
are disclosed. The particles are first placed in a solution of a first
monomer that forms a self-assembling monolayer on the particles thereby
forming coated particles. The coated particles are then suspended in a
second solution that includes a chemical species and an initiator for
oxidative polymerization. The chemical species has a higher oxidation
potential than the monomers. In addition, the chemical species form a
homopolymer in the presence of the initiator that is covalently bound to
the first monomers. Particles of semiconductors such as TiO.sub.2,
SiO.sub.2, SnO.sub.2, Al.sub.2 O.sub.3 can be coated with polymers that
alter the bandgap energy of the semiconducting particles and/or provide
other useful surface chemistries.
Une méthode pour enduire des particules et les particules enduites obtenues de ce fait sont révélées. Les particules sont d'abord placées dans une solution d'un premier monomère qui forme une monocouche de art de l'auto-portrait-assembling sur les particules formant de ce fait les particules enduites. Les particules enduites sont alors suspendues dans une deuxième solution qui inclut des espèces chimiques et un initiateur pour la polymérisation oxydante. Les espèces chimiques a un potentiel plus élevé d'oxydation que les monomères. En outre, les espèces chimiques forment une homopolymère en présence de l'initiateur qui est en covalence lié aux premiers monomères. Des particules des semi-conducteurs tels que TiO.sub.2, SiO.sub.2, SnO.sub.2, Al.sub.2 O.sub.3 peuvent être enduites des polymères qui changent l'énergie de bandgap des particules semi-conductrices et/ou fournissent d'autres chimies extérieures utiles.